English
| Quantity: | |
|---|---|
XF-3152; XF-2412; XF2002; XF-1752;
产品物理指标及应用(Product Phy sical Indicators and Application)
产品 Product 指标 Specs | 羟值Hydroxyl Value | 酸值 Acid Value | 水份Moisture | 粘度 Viscosity | 应用领域 Application |
mgKOH/g
| mgKOH/g
| %
| mPa.s(25℃)
| ||
XF-3152 | 315±15 | ≤2.0 | ≤0.1 | 3000±500 | 喷涂/家电/板材管道/仿木等 Spray Coating/Home Appliances/Panel Piping/Wood Imitation, etc. |
XF-2412 | 260±10 | ≤1.5 | ≤0.1 | 6000±1500 | 喷涂/板材/管道 Spray/Panels/Pipe |
XF-2002 | 195±5 | ≤1.0 | ≤0.1 | 10000-30000 | 喷涂/PIR板材 Spray/PIR Panels |
XF-1752 | 175±10 | ≤1.0 | ≤0.1 | <5000 | 喷涂/PIR板材 Spray/PIR Panels |
聚氨酯喷涂推荐典型配方（Recommended Typical Formula for Polyurethane Spraying）
Polyester Polyol XF-3152 | 70 |
低羟值高官低粘度聚醚多元醇 (4110) Low Hydroxyl Value, High Functionality, Low Viscosity Polyether Polyol (4110) | 30 |
硬泡硅油 (Rigid Foam Silicone Oil) | 2 |
阻燃剂 (Flame Retardant ) TCPP | 35 |
催化剂(Catalyst) PC5 | 2.5 |
催化剂(Catalyst) A33 | 3 |
催化剂(Catalyst)TMR-2 | 1.5 |
水 Water | 2.5 |
发泡剂 245fa (Blowing Agent 245fa) | 15 |
手工发泡物理参数（Phy sical Parameters of Hand Foaming）
项目 Iterm | 数值 Value |
物料温度 (℃ )
Material Temperature | 常温 Room Temperature |
黑白料比例
Ratio of Black Material to White
Material | 1/1 |
乳白时间 Creaming Time（s） | 3-5 |
纤维时间 Fiber Time（s） | 6-9 |
不粘时间 Tack-Free Time（s） | 10-14 |
喷涂制品物理性能参数（Physical property parameters of sprayed products）
泡沫密度(Foam Density）Kg/m3 | 38-40 | |
压 缩 强 度 (Compressive strength) Kpa(∥⊥) | ≥130 | |
尺寸 稳 定 性(Dimensional Stability) % | -30℃48hr | ≤1 |
70℃24hr | ≤1 | |
导热系数W/(m.K) | ≤0.022 | |
氧指数% | 25.5-26.5 | |
※备注：以上参数是基于实验室数据，实际参数可能随着配方及工艺环境变化而改变，仅供参考！
※Note: The above parameters are based on laboratory data. Actual parameters may change with the formula and process environment, and are for reference only!
产品物理指标及应用(Product Phy sical Indicators and Application)
产品 Product 指标 Specs | 羟值Hydroxyl Value | 酸值 Acid Value | 水份Moisture | 粘度 Viscosity | 应用领域 Application |
mgKOH/g
| mgKOH/g
| %
| mPa.s(25℃)
| ||
XF-3152 | 315±15 | ≤2.0 | ≤0.1 | 3000±500 | 喷涂/家电/板材管道/仿木等 Spray Coating/Home Appliances/Panel Piping/Wood Imitation, etc. |
XF-2412 | 260±10 | ≤1.5 | ≤0.1 | 6000±1500 | 喷涂/板材/管道 Spray/Panels/Pipe |
XF-2002 | 195±5 | ≤1.0 | ≤0.1 | 10000-30000 | 喷涂/PIR板材 Spray/PIR Panels |
XF-1752 | 175±10 | ≤1.0 | ≤0.1 | <5000 | 喷涂/PIR板材 Spray/PIR Panels |
聚氨酯喷涂推荐典型配方（Recommended Typical Formula for Polyurethane Spraying）
Polyester Polyol XF-3152 | 70 |
低羟值高官低粘度聚醚多元醇 (4110) Low Hydroxyl Value, High Functionality, Low Viscosity Polyether Polyol (4110) | 30 |
硬泡硅油 (Rigid Foam Silicone Oil) | 2 |
阻燃剂 (Flame Retardant ) TCPP | 35 |
催化剂(Catalyst) PC5 | 2.5 |
催化剂(Catalyst) A33 | 3 |
催化剂(Catalyst)TMR-2 | 1.5 |
水 Water | 2.5 |
发泡剂 245fa (Blowing Agent 245fa) | 15 |
手工发泡物理参数（Phy sical Parameters of Hand Foaming）
项目 Iterm | 数值 Value |
物料温度 (℃ )
Material Temperature | 常温 Room Temperature |
黑白料比例
Ratio of Black Material to White
Material | 1/1 |
乳白时间 Creaming Time（s） | 3-5 |
纤维时间 Fiber Time（s） | 6-9 |
不粘时间 Tack-Free Time（s） | 10-14 |
喷涂制品物理性能参数（Physical property parameters of sprayed products）
泡沫密度(Foam Density）Kg/m3 | 38-40 | |
压 缩 强 度 (Compressive strength) Kpa(∥⊥) | ≥130 | |
尺寸 稳 定 性(Dimensional Stability) % | -30℃48hr | ≤1 |
70℃24hr | ≤1 | |
导热系数W/(m.K) | ≤0.022 | |
氧指数% | 25.5-26.5 | |
※备注：以上参数是基于实验室数据，实际参数可能随着配方及工艺环境变化而改变，仅供参考！
※Note: The above parameters are based on laboratory data. Actual parameters may change with the formula and process environment, and are for reference only!